AQUAFIN®-2C
2-component, flexible, polymer modified, Cementitious Waterproofing
Properties:
AQUAFIN-2C= is a flexible, 2-component, polymer modified, cement-based waterproof protective coating. It has an excellent adhesion, abrasion resistance, weatherproofing & waterproofing properties providing seamless protective coats
Key Features and Benefits:
- Easy fo use and to apply
- Environmentally friendly
- UV-stable
- Resists hydrostatic pressure (> 5 bars}
- Crack bridging ability
- Flexible Enables substrates to breathe
- Can be applied to damp surfaces
- Abrasion resistant
- Selt-curing
- Active barrier to Carbon Dioxide (CO9}
- Stands up to pedestrian and light traffic
Uses:
- AQUAFIN-2C is an economic, flexible polymer modified cement-based protective coating for above & below grade, horizontal or vertical surfaces for:
- Water structures
- Sewage treatment plants
- Basement walls
- Balconies, plaza deck
- Underneath tile adhesive mortars (showers, sanitary
rooms, kitchens, swimming pools, etc.] - Wastewater treating plants
- Reinforced concrete structures
- Water tanks and reservoirs
- All similar works
AQUAFIN-2C is a stancalone product. It can be used exposed or over-coated with flexible or rigid mortars (use a separation layer), stuccos or coatings for uniform appearance. It bridges shrinkage cracks. Larger static {non-moving) or dynamic {moving) cracks can be sealed with ASO-JointTape-2000 or ASO-Joint
Tape-2000-S in conjunction with AQUAFIN-2C.
Product Exposure:
- rain, vertical surfaces, after approx. 3 hrs
- rain, horizontal surfaces, minimum 6 hrs
- foot traffic after approx 1day
- tile mortar and tiles after approx 1 day
- hydrostatic pressure after reaching Shore A Hardness 85 (between 3-7 days]
- back filling after aoprox. 3 days “) at +20 ° C and 60% humidity
Technical Specifications:
All data are averages of several tests under laboratory conditions. In practice, climatic variations such as temperature, humidity, and porosity of substrate may affect these values.
- Mixing ratio: 25 kg powder (comp. |} to 10
kg liquid {comp. Il} - Permeability: resistant up to 50m water head (positive side}
- Water vapour diffusion p-value: 1000
- Adhesive strength: O06N/mm2 at 28d
- Tensile elongation: 30 % at +20 °C
Product Application:
The substrate must be sound, clean, and free from voids, gaping cracks or ridges and open pored [like fine sand paper]. Remove bond breakers, such as oil, grease, dirt, loose particles, remains of form oils, water repellents, rust or other coatings by water blasting or wet or dry sandblasting. Repair holes, defects, irregular surfaces, weak mortar joints, etc. with a patching mortar. Round edges at vertical external joints. Close large open pores and joint recesses of CMU blocks and joint unevenness in brick walls with sand/cement mortar before applying AQUAFIN-2C.
Pre-dampen all absorbtive substrates (excluding drywall or similar} with clean water to saturated surface dry (SSD} condition prior to application. Remove all standing surface water. Seal dry, dusty or very absorptive surtaces (i.e. drywall, gypsum} with one coat liquid component, diluted with water 1:4 to 1:5.
A. Mixing ratio by weight:
25 kg powder to 10 kg liquid
B. Mixing ratio by volume:
approximately 2.5 parts powder to | part liquid.
Pour UNIFLEX-2C liquid into a clean container, add AQUAFIN-2C powder and stir to a lump free creamy consistency with a strong, slow speed (300 rom} mechanical mixer.
NOTE: Do not apply AQUAFIN-2C at temperatures below +5 °C.